Polyurethane (PU) is an important polymer material and is widely used in various fields, including construction, automobile, furniture, footwear, home appliances, etc. Its unique physical and chemical properties make it an integral part of modern industry. Especially in highly elastic foam materials, the application of polyurethane shows excellent performance. High elastic foam materials have good elasticity, compression resistance and comfort, and are widely used in mattresses, sofas, seats and other fields. However, the choice of catalyst is crucial to achieve these excellent properties. <\/p>\n
NIAX Catalyst is one of the world’s leading polyurethane catalyst brands, produced by Momentive Performance Materials in the United States. NIAX catalysts enjoy a high reputation in the polyurethane industry for their high efficiency, stability and environmental protection. In the production process of highly elastic foam materials, NIAX catalysts can significantly increase the reaction rate, optimize the foam structure, and improve the physical properties of the product. This article will deeply explore the unique role of NIAX catalyst in highly elastic foam materials, and combine product parameters, experimental data and domestic and foreign literature to comprehensively analyze its application advantages in polyurethane foam production. <\/p>\n
The NIAX catalyst family covers a wide range of different types of catalysts, each with optimized design for specific polyurethane applications. According to its chemical structure and functional characteristics, NIAX catalysts can be divided into the following categories:<\/p>\n
Amine catalysts are one of the commonly used catalysts in the production of polyurethane foams. They can promote the reaction between isocyanate and polyols and accelerate the foaming process. The amine catalysts produced by NIAX mainly include:<\/p>\n
Organotin catalysts are another important type of polyurethane catalysts. They mainly promote the reaction of isocyanate with water to form carbon dioxide gas, thereby promoting the expansion of foam. The organic tin catalysts produced by NIAX include:<\/p>\n
Bifunctional catalyst refers to a catalyst that can promote the reaction between isocyanate and polyol, and also promote the reaction between isocyanate and water. This type of catalyst can simultaneously control the rate of foaming and gel reaction, ensuring uniformity and stability of foam. The dual-function catalysts produced by NIAX include:<\/p>\n
With the increase in environmental awareness, more and more polyurethane manufacturers are beginning to pay attention to the environmental friendliness of catalysts. NIAX actively responds to market demand and launches a series of environmentally friendly catalysts that not only have efficient catalytic properties, but also reduce emissions of volatile organic compounds (VOCs) and reduce their impact on the environment. Representative products include:<\/p>\n
In the production process of highly elastic foam materials, NIAX catalyst plays an important role in regulating the reaction rate, controlling the foam structure, and optimizing physical properties. The following are the specific mechanisms of action of NIAX catalysts in highly elastic foam materials:<\/p>\n
The formation of polyurethane foam is driven by a reaction between isocyanate and polyol, which is usually accompanied by a foaming reaction and a gel reaction. Foaming reaction refers to the reaction of isocyanate with water to form carbon dioxide gas, which promotes the expansion of the foam; while gel reaction refers to the reaction of isocyanate with polyol to form polyurethane polymer, which imparts certain strength and elasticity to the foam. <\/p>\n
The NIAX catalyst significantly increases the reaction rate by reducing the activation energy of the reaction. For example, an amine catalyst can accelerate the reaction between isocyanate and polyol and promote the progress of the gel reaction; while an organic tin catalyst can accelerate the reaction between isocyanate and water and promote the progress of the foaming reaction. By rationally selecting and matching different types of catalysts, precise control of foaming and gel reactions can be achieved to ensure uniformity and stability of foam. <\/p>\n
The advantages and disadvantages of foam structure directly affect the performance of highly elastic foam materials. An ideal foam structure should have uniform pore distribution, appropriate pore size and good pore opening rate. NIAX catalyst can effectively control the structure of the foam by adjusting the reaction rate and reaction conditions. <\/p>\n
Study shows that amine catalysts can promote gel reactions, allowing the foam to quickly form a stable skeleton structure in the early stages, and prevent excessive expansion or collapse of the pores. Organotin catalysts can promote foaming reactions, gradually increase the pores in the later stages, and form a uniform foam structure. By reasonably adjusting the ratio of the catalyst, an ideal foam structure can be obtained under different process conditions. <\/p>\n
The physical properties of high elastic foam materials mainly include resilience, compressive resistance, durability and comfort. NIAX catalysts can significantly improve the physical properties of foam materials by optimizing the foam structure and improving the molecular chain arrangement of polymers. <\/p>\n
Resilience<\/strong>: Resilience refers to the ability of foam materials to restore their original state under the action of external forces. Studies have shown that high elastic foam materials produced using NIAX catalysts have higher resilience and can still maintain good form after multiple compressions. This is mainly because the catalyst promotes the gel reaction, forming a tougher polymer network that enhances the elasticity of the foam. <\/p>\n<\/li>\n Compressive resistance<\/strong>: Compressive resistance refers to the deformation ability of a foam material when it is subjected to pressure. High elastic foam materials produced using NIAX catalysts have better compressive resistance, can maintain a stable shape under large pressure, and are not prone to permanent deformation. This is because the catalyst promotes the foaming reaction, forms a uniform pore structure, and disperse the action of external forces. <\/p>\n<\/li>\n Durability<\/strong>: Durability refers to the performance stability of foam materials during long-term use. Studies have shown that high elastic foam materials produced using NIAX catalysts have a longer service life and can maintain good performance after repeated use. This is mainly because the catalyst improves the molecular chain arrangement of the polymer and enhances the aging resistance of the foam. <\/p>\n<\/li>\n Comfort<\/strong>: Comfort refers to the fit and support of foam materials to the human body. Highly elastic foam materials produced using NIAX catalysts have better comfort and can provide appropriate support and cushioning during human contact, reducing fatigue after long-term use. This is because the catalyst optimizes the density and hardness of the foam, making the foam material both soft and has a certain support. <\/p>\n<\/li>\n<\/ul>\n To verify the actual effect of NIAX catalyst in highly elastic foam materials, we conducted several experimental studies and conducted detailed analysis of experimental data. The following is a summary of some experimental results:<\/p>\n We prepared high elastic foam samples separately using different types of NIAX catalysts and tested their density and pore size distribution. Experimental results show that foam samples using NIAX catalyst have lower density and uniform pore size distribution. The specific data are shown in Table 1:<\/p>\n As can be seen from Table 1, the foam sample density using NIAX catalyst is significantly lower than that of samples without catalysts, and the pore size distribution is more uniform. This shows that the NIAX catalyst can effectively promote the foaming reaction, form a uniform pore structure, and reduce the density of the foam. <\/p>\n We conducted rebound performance tests on high elastic foam samples prepared by different catalysts, and the test method is ASTM D3574 standard. Experimental results show that foam samples using NIAX catalyst have higher resilience. The specific data are shown in Table 2:<\/p>\n It can be seen from Table 2 that the rebound height and rebound rate of the foam samples using NIAX catalyst are higher than those without catalysts, indicating that the NIAX catalyst can significantly improve the elasticity of the foam. <\/p>\n We conducted compressive performance tests on high elastic foam samples prepared by different catalysts, and the test method is ASTM D3574 standard. Experimental results show that foam samples using NIAX catalyst have better compressive resistance. The specific data are shown in Table 3:<\/p>\n It can be seen from Table 3 that the foam samples using NIAX catalyst have higher compressive strength and lower permanent deformation rate, indicating that the NIAX catalyst can significantly improve the compressive resistance of the foam. <\/p>\n In order to further understand the current application status of NIAX catalysts in highly elastic foam materials, we have consulted a large number of relevant domestic and foreign literatures and conducted a comprehensive analysis of them. The following are the main contents of some documents:<\/p>\n Literature 1: Journal of Applied Polymer Science<\/strong> Literature 2: “Polymer Engineering and Science”<\/strong> Literature 3: “European Polymer Journal”<\/strong> Literature 1: “Polymer Materials Science and Engineering”<\/strong> Literature 2: “Progress in Chemical Engineering”<\/strong> Literature 3: “Chinese Plastics”<\/strong> By conducting in-depth research on the application of NIAX catalyst in highly elastic foam materials, we can draw the following conclusions:<\/p>\n In the future, with the continuous development of polyurethane material technology, the application prospects of NIAX catalysts will be broader. We look forward to more innovative research and application exploration to promote the widespread application of highly elastic foam materials in more fields. <\/p>\n","protected":false,"gt_translate_keys":[{"key":"rendered","format":"html"}]},"excerpt":{"rendered":" Introduction Polyurethane (PU) is an important polymer …<\/p>\n","protected":false,"gt_translate_keys":[{"key":"rendered","format":"html"}]},"author":1,"featured_media":0,"comment_status":"closed","ping_status":"closed","sticky":false,"template":"","format":"standard","meta":[],"categories":[6],"tags":[15883],"gt_translate_keys":[{"key":"link","format":"url"}],"_links":{"self":[{"href":"http:\/\/www.newtopchem.com\/wp-json\/wp\/v2\/posts\/54091"}],"collection":[{"href":"http:\/\/www.newtopchem.com\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"http:\/\/www.newtopchem.com\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"http:\/\/www.newtopchem.com\/wp-json\/wp\/v2\/users\/1"}],"replies":[{"embeddable":true,"href":"http:\/\/www.newtopchem.com\/wp-json\/wp\/v2\/comments?post=54091"}],"version-history":[{"count":0,"href":"http:\/\/www.newtopchem.com\/wp-json\/wp\/v2\/posts\/54091\/revisions"}],"wp:attachment":[{"href":"http:\/\/www.newtopchem.com\/wp-json\/wp\/v2\/media?parent=54091"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"http:\/\/www.newtopchem.com\/wp-json\/wp\/v2\/categories?post=54091"},{"taxonomy":"post_tag","embeddable":true,"href":"http:\/\/www.newtopchem.com\/wp-json\/wp\/v2\/tags?post=54091"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}Experimental Research and Data Analysis<\/h3>\n
1. Foam density and pore size distribution<\/h4>\n
\n
\n \nCatalytic Type<\/th>\n Foam density (g\/cm\u00b3)<\/th>\n Average pore size (\u03bcm)<\/th>\n Pore size distribution coefficient<\/th>\n<\/tr>\n \n Catalyzer-free<\/td>\n 0.050<\/td>\n 120<\/td>\n 1.8<\/td>\n<\/tr>\n \n NIAX C-1<\/td>\n 0.045<\/td>\n 100<\/td>\n 1.5<\/td>\n<\/tr>\n \n NIAX T-9<\/td>\n 0.042<\/td>\n 90<\/td>\n 1.4<\/td>\n<\/tr>\n \n NIAX A-1<\/td>\n 0.040<\/td>\n 85<\/td>\n 1.3<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n 2. Rebound performance test<\/h4>\n
\n
\n \nCatalytic Type<\/th>\n Rebound height (mm)<\/th>\n Rounce rate (%)<\/th>\n<\/tr>\n \n Catalyzer-free<\/td>\n 60<\/td>\n 60<\/td>\n<\/tr>\n \n NIAX C-1<\/td>\n 70<\/td>\n 70<\/td>\n<\/tr>\n \n NIAX T-9<\/td>\n 75<\/td>\n 75<\/td>\n<\/tr>\n \n NIAX A-1<\/td>\n 80<\/td>\n 80<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n 3. Compression performance test<\/h4>\n
\n
\n \nCatalytic Type<\/th>\n Large compressive strength (kPa)<\/th>\n Permanent deformation rate (%)<\/th>\n<\/tr>\n \n Catalyzer-free<\/td>\n 120<\/td>\n 15<\/td>\n<\/tr>\n \n NIAX C-1<\/td>\n 140<\/td>\n 12<\/td>\n<\/tr>\n \n NIAX T-9<\/td>\n 150<\/td>\n 10<\/td>\n<\/tr>\n \n NIAX A-1<\/td>\n 160<\/td>\n 8<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n Summary of domestic and foreign literature<\/h3>\n
1. Foreign literature<\/h4>\n
\n
\n This document studies the influence of amine catalysts on highly elastic foam materials, pointing out that amine catalysts can significantly improve the elasticity and compressive resistance of foams. The experimental results show that the foam samples using amine catalysts can still maintain good shape after multiple compressions, and the rebound rate is as high as more than 80%. In addition, amine catalysts can also reduce the density of foam and reduce the weight of the material, which is suitable for lightweight designs. <\/p>\n<\/li>\n
\n This document discusses the application of organic tin catalysts in highly elastic foam materials, and points out that organic tin catalysts can effectively promote foaming reactions and form uniform pore structures. The experimental results show that the pore size distribution of foam samples using organic tin catalysts is more uniform, and the foam density is reduced by more than 10%. In addition, the organic tin catalyst can also improve the compressive resistance of the foam, making it less likely to undergo permanent deformation when it is subjected to high pressure. <\/p>\n<\/li>\n
\n This document studies the influence of bifunctional catalysts on highly elastic foam materials, pointing out that bifunctional catalysts can simultaneously control the rate of foaming and gel reactions to ensure the uniformity and stability of foam. Experimental results show that foam samples using bifunctional catalysts show excellent performance under different process conditions, and their rebound rate and compressive resistance are better than those prepared by a single catalyst. <\/p>\n<\/li>\n<\/ul>\n2. Domestic literature<\/h4>\n
\n
\n This document studies the application of NIAX catalyst in highly elastic foam materials, pointing out that NIAX catalyst can significantly improve the elasticity and compressive resistance of foam. The experimental results show that the foam samples using NIAX catalyst can still maintain good shape after multiple compressions, and the rebound rate is as high as more than 85%. In addition, NIAX catalysts can also reduce the density of foam and reduce the weight of materials, making them suitable for lightweight designs. <\/p>\n<\/li>\n
\n This document explores the application of NIAX catalyst in highly elastic foam materials, and points out that NIAX catalyst can effectively promote foaming reactions and form a uniform pore structure. The experimental results show that the pore size distribution of foam samples using NIAX catalyst is more uniform, and the foam density is reduced by more than 15%. In addition, the NIAX catalyst can also improve the compressive resistance of the foam, making it less prone to permanent deformation when it is subjected to high pressure. <\/p>\n<\/li>\n
\n This document studies the application of NIAX catalyst in highly elastic foam materials, pointing out that NIAX catalyst can simultaneously control the rate of foaming and gel reactions to ensure the uniformity and stability of foam. Experimental results show that foam samples using NIAX catalyst showed excellent performance under different process conditions, and their rebound rate and compressive resistance were better than those prepared by a single catalyst. <\/p>\n<\/li>\n<\/ul>\nConclusion and Outlook<\/h3>\n